Customizable Ceramic Fiber Vacuum Alien Products

• Customization: Available
• Usage: High Temperature Insulating Material
• Temprature Classification: 1600℃
• Model NO.: CT-1260
• Chemical Composition: SiO2, Al2O3.SiO2, Al2O3
• Shape: According The Drawings
• Manufacturing Technique: Jilt Silk Rug
• Kind: Ordinary Ceramic Fiber
• Colour: White
• Modulus of Rupture: ≥0.2
• Heating Shrinkage % (Soaking for 24 H): ≤2.0 (1500℃X6h)
• Thermal Conductivity(W/M.K): 1000℃ 0.28
• Al2O3: ≥65
• Al2O3+Sio2: ≥99
• Transport Package: Wood Case/Pallet
• Specification: according the drawings
• Trademark: Ceratec
• Origin: Jiangsu
• HS Code: 6806101000
• Production Capacity: 5000PCS/Month
• Package Size: 120.00cm * 110.00cm * 100.00cm
• Package Gross Weight: 100.000kg

Product Description

Ceramic fiber vacuum formed shape
 

Product Description

 

1. VF shapes are produced from corresponding level refractory fibre mixture through vaccum forming.
2. VF shapes without burning is free shear and bending. They are the ideal energy-efficient insulation materials of a furnace, piping and other equipment.
3. Support Surface hardening or completely hardening to every level VF shapes according to customers' demand.

 

Products Features

 

1. Low thermal conductivity, low thermal capacity
2. High crushing strength, good toughness
3. Good resistance to air scour
4. A wide range of sizes and forms, including tubes, cones, domes ,etc.
5. Produced to individual customer requirements
6. Easy cutting and installation

 

Typical Application

 

1. Observation hole, the thermonmeter hole of industrial kiln
2. Combustion chamber
3. Custom electric element laboratory furnaces
4. Headboxes and launders used in aluminum
5. Radiant heat insulation for commercial and industrial heaters.

 

Detailed Photos

Data Sheet

Name		CT 1000	CT 1260	CT 1350	CT 1430	CT 1600	CT 1700	CT 1800
Classification Temperature (ºC)		1000	1260	1350	1430	1600	1700	1800
Density (kg/m³)		300-600				400-700
Heating Shrinkage % (Soaking for 24 h)		≤3.0 (900ºCx24h)	≤3.0 (1000ºCx24h)	≤3.0 (1100ºCx24h)	≤3.0 (1300ºCx24h)	≤2.0 (1500ºCx6h)	≤2.0 (1500ºCx6h)	≤2.0 (1550ºCx6h)
Modulus of Rupture (MPa)		≥0.6	≥0.6	≥0.6	≥0.6	≥0.2	≥0.2	≥0.2
Thermal Conductivity(W/m.k)	400ºC	0.08	0.08	0.08	0.08	0.09	0.09	0.09
	600ºC	0.12	0.12	0.12	0.12	0.14	0.14	0.14
	800ºC	0.16	0.16	0.16	0.16	0.20	0.20	0.20
	1000ºC	-	-	0.23	0.23	0.28	0.28	0.28
Chemical Composition  (After burning)	Al2O3	≥37	≥41	≥43	≥37	≥65	≥70	≥72
	Al2O3+SiO2	≥95	≥97	≥98	≥84	≥99	≥99	≥99
	Al2O3+SiO2+ZrO2	-	-	-	≥98	-	-	-
	ZrO2	-	-	-	≥11	-	-	-
	CrO	≤2.0	≤2.0	≤2.0	≤2.0	≤1.0	≤1.0	≤1.0