Heat Resistant Fireproof Board Insulation for Pottery Kiln China Export

• Customization: Available
• Usage: High Temperature Insulating Material
• Temprature Classification: 1260℃
• Model NO.: CT-1100
• Chemical Composition: SiO2, Al2O3.SiO2, Al2O3
• Shape: Ceramic Fiber Board
• Manufacturing Technique: Jilt Silk Rug
• Kind: Ordinary Ceramic Fiber
• Color: White
• Density: 200
• Temp: 1260
• Sio2: Sio2
• Transport Package: Pallet
• Specification: 8~50mm
• Trademark: Cera Tec
• Origin: Shandong
• HS Code: 6806101000
• Production Capacity: 5000PCS/Week
• Package Size: 120.00cm * 110.00cm * 100.00cm
• Package Gross Weight: 200.000kg

Product Description

Heat Resistant Fireproof Insulation Board for Pottery Kiln China Export

Product Description

 

1. All kinds of ceramic fibre board adopt ceramic fibre which is in Corresponding temperature level as raw material, through the large automatic vacuum filter molding machine to shape them, then they will be done after special baking.
2. The product with good toughness and strength appears flattening and the ceramic material distributes uniformity, it also has excellent Thermal insulation performance.
3. Heating is not inflated, light, construction convenient, free shear and bending, is the ideal energy-efficient insulation materials of a furnace, piping and other equipment.

Products Features

 

1. Low thermal conductivity and ow heat storage.
2. High temperature stability and resistant to thermal shock.
3. High crushing strength and good toughness.
4. Allow machining and cutting, easy application.
5. Resistant to airflow erosion.

Typical Application

 

1. All kinds of industrial furnace hot face and back face insulation
2. Kiln linerof the high-temperature furnace, kiln cars, door damper, furnace temperature to separate plate.
3. Deep processing products molding mould, like Craft glass etc
4. Astronavigation,Shipbuilding heat insulation,fireproofing, sound proofing, insulation.

Data Sheet

 

Type	CT-1000	CT-1260	CT-1360	CT-1430	CT-1500
Classification temperature (ºC)	1100	1260	1360	1430	1500
Color	white	white	white	white	Light green
Density (kg/m³)	280	280	280	280	280
Linear shrinkage after firing % (ºC*24h)	≤4 (1000ºC)	≤4 (1200ºC)	≤4 (1300ºC)	≤4 (1400ºC)	≤4 (1400ºC)
Ignition lost (at 1000ºC*5hr) LOI%	5	5	5	5	5
Thermal Conductivity (W/m.k)	0.085(400ºC)   0.132(600ºC)   0.150(800ºC)	0.085(400ºC)   0.132(600ºC)   0.191(1000ºC)	0.085(400ºC)   0.132(600ºC)   0.191(1000ºC)	0.085(400ºC)   0.132(600ºC)   0.191(1000ºC)	0.085(400ºC)   0.132(600ºC)   0.191(1000ºC)
Rupture strength Mpa	0.5	0.5	0.5	0.5	0.5
Chemical composition %
AL2O3	42-44	45-46	52-55	39-40	43
AL2O3+SIO2	96	98	99	99	99
ZrO2	-	-	-	12	-
Cr2O3	-	-	-	-	2.5-3.0