CT-30 Unfired Refractory Brick for Rotary Kiln

• Customization: Available
• Feature: Long Time Materials
• Refractoriness (℃): 1580< Refractoriness< 1770
• Model NO.: CT-30
• Color: White
• Density: 1000kg/M3
• Material1: Al2O3, Sio2, Fe2o3
• Classification Temperature: 1550ºC
• Type: Heat-Resistant Material
• Material: Alumina Block
• Transport Package: Pallet
• Specification: 230*114*65/65
• Trademark: Cera Tec
• Origin: Jiangsu
• HS Code: 6902200000
• Production Capacity: 6000PCS/Week

Product Description

CT-30 Unfired Refractory Brick for Rotary Kiln

Description

1. CT firebricks are made from high-purity refractory clays, temperature of use ranging from 1100 ^oC to 1700 ^oC, each grade is formulated to meet specific thermal and physical requirements.
2. With graduated additions of alumina for higher temperature products
3. Carefully grade d organic filler
4. The organic filler burns out during manufacture to give a uniform, control pore structure.

Features

1. low thermal conductive, low heat storage
2. purity
3. good thermal insulation, enable the use of thin-walled constructions
4. the good alumina contents confer good refractoriness
5. iow iron and alkali fluxcontent contributes to their stability to reducing atmosphere
6. these can be machined to special shapes, incurring fewer sections and joints

Typical Application

1. Recommended for use as primary hot face refractory lining or as back-up insulation behind other refractories in furnaces, kiln, flues, heaters, regenerators, stress relieving furnaces,etc

 

Material Type	CT-30
Classification Temperature (ºC)	1550±30
Density (kg/m3)	1000±50
Cold Crushing Strength (MPa)	2.7±0.1
Cold Modulus Rupture (MPa)	1.6±0.1
Permanent Linear Change(1230ºC×4h)	0.8±0.1%
Linear Thermal Expansion	0.49±0.05%
Thermal Conductivity ºC
Mean Temperature, ºC	W/(m·k)
400	0.38
600	0.41
800	0.43
1000	0.45
Chemical Analysis	%
Al2O3	70±2
Fe2O3	0.7±0.1
SiO2	25±2
TiO2	0.45±0.01
CaO	0.4±0.01
MgO	0.1±0.01
K2O	0.56±0.01
Na2O	0.1±0.01
Dimensional Tolerances(mm)	±0.5