CT-23 Insulation Fire Brick for Furnace Lining

• Customization: Available
• Feature: Long Time Materials, Instant Materials
• Refractoriness (℃): 1580< Refractoriness< 1770
• Model NO.: CT-23
• Shape: Brick
• Color: White
• Type: Heat-Resistant Material
• Material: Alumina Block
• Transport Package: Pallet
• Specification: 230*114*65/75
• Trademark: Cera Tec
• Origin: Jiangsu
• HS Code: 6902900000
• Production Capacity: 60000 Pieces / Week

Product Description

CT-23 Insulation Fire Brick for Furnace Lining

Description

1. CT firebricks are made from high-purity refractory clays, temperature of use ranging from 1100 ^oC to 1700 ^oC, each grade is formulated to meet specific thermal and physical requirements.
2. With graduated additions of alumina for higher temperature products
3. Carefully grade d organic filler
4. The organic filler burns out during manufacture to give a uniform, control pore structure.

Features

1. low thermal conductive, low heat storage
2. purity
3. good thermal insulation, enable the use of thin-walled constructions
4. the good alumina contents confer good refractoriness
5. iow iron and alkali fluxcontent contributes to their stability to reducing atmosphere
6. these can be machined to special shapes, incurring fewer sections and joints

Typical Application

1. Recommended for use as primary hot face refractory lining or as back-up insulation behind other refractories in furnaces, kiln, flues, heaters, regenerators, stress relieving furnaces,etc

 

Material Type	CT-23
Classification Temperature (ºC)	1250±30
Density (kg/m3)	500±50
Cold Crushing Strength (MPa)	1.1±0.2
Cold Modulus Rupture (MPa)	0.8±0.2
Permanent Linear Change(1230ºC×4h)	0.4±0.1%
Linear Thermal Expansion	0.46±0.05%
Thermal Conductivity ºC
Mean Temperature, ºC	W/(m·k)
400	0.16
600	0.19
800	0.22
1000	0.25
Chemical Analysis	%
Al2O3	36.3±2
Fe2O3	0.98±0.1
SiO2	60±2
TiO2	0.7±0.01
CaO	0.55±0.01
MgO	0.16±0.01
K2O	0.85±0.01
Na2O	0.3±0.01
Dimensional Tolerances (mm)	±0.5